MR Plywood
Made from High quality veneers of uniform thickness bonded with urea melamine formaldehyde resin with Addition of chemicals.
APPLICATION: Suitable for furniture, wall paneling, cupboards, partition, shelves, celling etc.
BWR Plywood
Manufacture with veneers of uniform thickness of high density Neem timber dried on mechanical drier, stress relieved, bonded with the best quality phenol formaldehyde and then treated with chemical and make it termite and wood boring insects proof.
APPLICATION: Suitable for home, office, industry, kitchen, paneling, bus and truck bodies, railway coaches etc.
Thickness: 6mm, 8mm, 12mm, 15mm, 16mm, 18mm,
SIZES(in Mtrs.): 2.44X1.22 / 2.44X0.92 / 2.14X1.22 / 2.14X0.92
(Specific thickness and Sizes may be provided against specific order.)
TECHNICAL SPECIFICATION
MR/BWR Grad Plywood IS:303
| M.R. | B.W.R | ||||
| SI.No | Test | I.S. Requirement | Result | I.S. Requirement | Result |
|---|---|---|---|---|---|
| 1 | Moisture Content | 5 to 15% | 10% | 5 to 15% | 10% |
| 2 | Static Bending Strength: I.Moduls of Elasticity (N/mm2) a)Along the Grain b)Across the Grain II.Moduls of Rupture(N/mm2) a)Along the Grain b)Across the Grain |
Min. 3600;Avg 4000 Min. 1800;Avg 2000 Min. 27; Avg 30 Min.13; Avg 15 |
4700 2200 42 20 |
Min. 4500;Avg 5000 Min. 2200;Avg 2500 Min. 36; Avg 40 Min.18;Avg 20 |
6500 3300 48 24 |
| 3 | Glue Shear Strength (In Dry State) | Min.Average 1000 Newton Individual 800 Newton |
1230 Newton 950 Newton |
Min.Average 1350 Newton Individual 1100 Newton |
1550 Newton 1330 Newton |
| 4 | Glue Shear Strength (In Wet State) | Min.Average 800 Newton Individual 650 Newton |
970 Newton 840 Newton |
Min.Average 1000 Newton Individual 800 Newton |
1190 Newton 1010 Newton |
| 5 | Glue Shear Strength in Mycological | Min.Average 800 Newton Individual 650 Newton |
1100 Newton 870 Newton |
Min.Average 1000 Newton Individual 800 Newton |
1210 Newton 1100 Newton |
Note: The above result are based on the test standards